17-4PH / SUS630 Altzairu Herdoilgaitzezko barra
| DIN | ASTM | AISI | UNS | JIS | Beste batzuk |
| 1.4542 | |||||
| X5CrNiCuNb16-4 | 630. maila | 630 | S17400 | SUS 630 | 17-4PH |
| AMS 5643 | |||||
| AMS 5622 | |||||
| Z6CNU17-04 | |||||
| 10705GU-GV |
Konposizio kimikoa (%)
| C | Si | Mn | P | S | Cr | Ni | Mo | Beste batzuk |
|---|---|---|---|---|---|---|---|---|
| ≤ 0,07 | ≤ 1,00 | ≤ 1,00 | ≤ 0,040 | ≤ 0,030 | 15,0 ～ 17,0 | 3,00 ～ 5,00 | - | Cu 3,00 ～ 5,00 Nb + Ta 0,15 ～ 0,45 |
Ezaugarri mekanikoak
| Tratamendu termikoaren egoera | Trakzioa RM (MPa) | Etekina Rp0.2 (MPa) | Luzapena A (%) | Gurutzearen murrizketa hausturari buruzko atala Z (%) | Eragina AKV / AKU (J) | Brinell Gogortasuna (HBW) |
|---|---|---|---|---|---|---|
| Ezkutatua | ≤ 1034 | ≤ 650 | 6,0 ～ 15,0 | 30,0 ～ 60,0 | - | ≤ 363 |
| H900 | ≥ 1380 | ≥ 1275 | ≥ 14,0 | ≥ 50,0 | ≥ 20 | ≤ 420 |
| H925 | ≥ 1310 | ≥ 1200 | ≥ 14,0 | ≥ 54,0 | ≥ 34 | ≤ 409 |
| H1025 | ≥ 1170 | ≥ 1140 | ≥ 15,0 | ≥ 56,0 | ≥ 47 | ≤ 352 |
| H1075 | ≥ 1140 | ≥ 1035 | ≥ 16,0 | ≥ 58,0 | ≥ 61 | ≤ 341 |
| H1100 | ≥ 1035 | ≥ 930 | ≥ 17,0 | ≥ 58,0 | ≥ 61 | ≤ 332 |
| H1150 | ≥ 1000 | ≥ 860 | ≥ 19,0 | ≥ 60,0 | ≥ 68 | ≤ 311 |
| H1150 + H1150 | ≥ 965 | ≥ 760 | ≥ 20,0 | ≥ 60,0 | ≥ 108 | ≤ 302 |
| H1150M | ≥ 860 | ≥ 585 | ≥ 22,0 | ≥ 68,0 | ≥ 135 | ≤ 277 |
Formak eta formak:
Barra biribila (diametroa): 5,5 mm-tik 700 mm-ra
Hari hagaxka (Diametroa): 0,10 ~ 16mm
Barra karratua / barra laua: 5mm-tik 550mm-ra
Altzairuzko banda hotz ijeztatuaren bidez: T0.1 - 3mm X W5 - 650mm XL (edo bobina moduan)
Forjatutako eraztuna: OD200 ~ 1500mm X ID150 ~ 1250mm X H20 ~ 1250mm
Plaka astun / erdikoa beroan ijeztutako bidez: T50 - 200mm X W80- 1200mm X L1000-3000mm
Pieza forjatua: ardatz mailakatuak hegalekin / diskoekin / hodiekin / bareak / erroskilak / kuboak / OEM-en oinarritutako beste forma desberdinekin.
Luzera: luzera finkoa edo ausazko luzera edo bezeroaren eskakizun berezian oinarrituta.